Marianne. Senn (EMPA, Dübendorf, Zurich, Switzerland) & Christian. Degrigny (HE-Arc CR, Neuchâtel, Neuchâtel, Switzerland)
Construction element used for suspension of an altar crown (Fig. 1).
Abbey of Rheinau, Zürich, Zurich, Switzerland
Abbey of Rheinau, Zürich, Zurich
Canton of Zurich, Zurich
Not conserved (machine brushed)
Nothing to report.
Stratigraphic representation: none.
This sample is a section from the end of the wedge part (Fig. 2). The corrosion crust appears on the top side on Fig. 3.
P-rich iron and hypoeutectoid steel
Annealed after (hot) rolling
Empa (Marianne Senn)
IWT (Naila Hadzic), Wallisellen, Zurich
January 2008, material testing and security report
Nothing to report.
Metallography (nital etched and etched with Oberhoffer’s reagent), Vickers hardness testing, LA-ICP-MS, SEM/EDS.
The remaining metal (M1) is a P-rich iron (0.3-0.45 mass%) with two zones (M3) consisting of soft, hypoeutectoid steel (C content 0.2 mass%) (Fig. 3 and Table 1). The P-rich iron contains many elongated slag inclusions of various sizes forming parallel rows (Figs. 3 and 5). The number of slag inclusions is higher than in bloomery iron and their distribution is typical for rolled metal. A crack, partially filled by hammer scale and corrosion products, indicates a poor quality welding seam (Fig. 3). Below the inclusions the curve produced by forging is highlighted. In good quality wrought iron slag inclusions are small, uniformly distributed and have identical compositions (Boesenberg 2006, 622). This is not the case in this sample, but can be explained by the rudimentary rolling process of the 18th century. The chemical composition of the slag inclusions shows that iron oxides dominate, beside phosphorus oxide, calcium oxide and silica (Table 2). The composition is typical for slag formed by hearth refining of pig iron (Dillmann and L'Héritier 2007). During this process, the pig iron is oxidised. The oxidising elements are Si, P, Mn, V and Cr. The analyzed slag inclusions contain more Fe than most published ones. The high P content is similar to published examples from the 18th century (Dillmann and L'Héritier 2007, 1820). The high calcium oxide content, which is often combined with high silica content, could originate from the addition of both materials while refining the pig iron to better eliminate the P. In one of our measurements, only the silica concentration is high (Table 2). This can be interpreted as resulting from the addition of sand during forging. Etching with Oberhoffer’s reagent outlines the thick welding seam (M2, Fig. 6), the rolling direction and the P segregation. Etching with nital mainly shows a ferritic structure (Fig. 7). The grains vary in size (between ASTM grain sizes of 4 to 8) and are recrystallized. The ferrite shows local ghost structures, and includes Neumann bands and some needles (Figs. 8 and 9). These are typical structures of P-rich iron. The ghost structure is formed by a fast recrystallization of P-rich iron after heating above 1000°C. The Neumann bands indicate cold working. The hypoeutectoid steel consists of ferrite with lamellar pearlite (Fig. 10). The average hardness of the metal is HV1 185 (in the Empa test report a mean of HV10 175 was determined). The areas close to the welding seam are harder (ca. HV1 210). The calculated tensile strength based on HV1 175 is about 544N/mm2.
|Detection limit mg/kg||-||4||65||8||1||10||2||1||3||1||2||3||1||0.4||1||3||-|
Table 1: Chemical composition of the P-rich iron. Method of analysis: LA-ICP-MS, Lab Inorganic Chemistry, ETH.
|White plates (wustite)||steel||<||<||1.1||<||<||<||<||0.9||<||<||<||97||101||3.4|
Slag with platesand droplets
|Wustite in glass||P-rich iron||0.6||0.7||6.5||17||0.8||<||4.0||<||0.9||<||0.9||77||109||9.2|
|n. d.||P-rich iron||<||0.8||1.3||4.6||<||<||<||0.6||3.0||1.5||<||94||106||1.6|
|n. d.||P-rich iron||0.8||1.1||5.4||11||<||<||3.8||0.9||3.9||<||0.7||81||108||5.1|
|n. d.||P-rich iron||<||1||1.6||3.7||<||<||0.8||0.8||5.3||0.7||<||84||99||1.6|
|n. d.||P-rich iron||1.2||<||8.9||13||<||<||2.7||<||2.3||0.7||0.9||68||99||18|
|n. d.||P-rich iron||0.8||1.2||8.7||23||<||9.8||<||0.7||<||1.3||54||99||7.6|
Table 2: Chemical composition of the slag inclusions (mass %). Method of analysis: SEM/EDS, Laboratory of Analytical Chemistry, Empa.
Recrystallized grains, Newman bands, ghost structure
Nothing to report.
The corrosion crust is thin and irregular. It is restricted to one of the three surfaces. In bright field, the corrosion layer seems homogeneous and appears medium-grey with a fissure parallel to the metal surface (Fig. 11). Under polarised light the corrosion products near the metal surface are mostly red-orange (CP3), whereas in the outer layer they appear orange-brown (CP1) (Fig. 12). A dark-brown zone is visible between them (CP2) and contains bright inclusions with a chemical composition similar to wüstite (Table 3). This corresponds to corroded slag inclusions (internal markers). Chemical analysis (Table 3) and elemental mapping (Fig. 13) do not highlight a difference in composition of the corrosion layers, except for the corroded slag inclusions.
|Inner part, dark-brown corrosion layer (CP2)||34||<||61||96|
|Inner part, orange corrosion products (average of 2 similar analyses) (CP3)||34||<||64||99|
|Middle, orange corrosion products||36||0.6||64||101|
|Outer orange corrosion layer (average of 3 similar analyses) (CP1)||34||0.7||62||96|
Table 3: Chemical composition (mass %) of the corrosion crust (from Fig. 12). Method of analysis: SEM/EDS, Laboratory of Analytical Chemistry, Empa.
Fig. 11: Micrograph showing the metal - corrosion layer interface from Fig. 3 (reversed picture, detail), unetched, bright field. The grey corrosion layer contains bright inclusion rows. The area selected for elemental chemical distribution (Fig. 13) is marked by the red rectangle which expends beyond the micrograph,
Uniform - pitting
Nothing to report.
Corrected stratigraphic representation: none.
The wedge was rolled, hammered and annealed from a refined, P-rich wrought iron. It was welded from at least two parts. The C distribution is irregular and shows a zone of soft steel in the middle of the iron. The indoor corrosion seems superficial, but it is possible that the sample surface was cleaned before embedding (Hadzic 2008).
References on object and sample
References on analytic methods and interpretation
|2. Boesenberg, J.S. (2006) Wrought iron from the USS Monitor: mineralogy, petrology and metallography. Archaeometry 48-4, 613-631.
3. Dillmann, P., L'Héritier, M. (2007) Slag inclusions analyses for studying ferrous alloys employed in French medieval building: supply o materials and diffusion of smelting process. Journal of Archaeological Science 34, 1810-1823.
4. ASTM E112-13: Standard Test Methods for Determining Average Grain Size.